水热法制备MoO2纳米棒的自组装生长机理研究
【摘 要】
：
水热条件下，以双氧水和钼粉制备的过氧钼酸溶胶为钼源，乙醇为还原剂制备得到二氧化钼纳米棒。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)以及场发射高分辨透射电子显微镜(HRTEM)对产物的结构与形貌进行表征。
【机 构】
：
武汉理工大学材料研究与测试中心,材料科学与工程学院 湖北武汉430070
【出 处】
：
2014中国功能材料科技与产业高层论坛
【发表日期】
：
2014年2期
其他文献
海水环境下服役的混凝土会经历一系列物理和化学侵蚀过程。通过先进测试技术，表征了海水和淡水环境下混凝土孔结构和界面过渡区，采用压汞法和扫描电镜等先进技术探索了海水环境下混凝土孔结构和界面过渡区的演变规律以及矿物掺合料对混凝土孔结构和界面过渡区的改善作用。
Piezoresistivity of activated carbon reinforced cement-matrix composites incorporating styrene-butad
The piezoresistivity of activated nano-carbon reinforced cement-matrix composites (CBPCs) with different styrene-butadiene rubber (SBR) content are experimentally studied.An interesting phenomenon of
会议
Porous poly(1-naphthylamine) were synthesized by interfacial polymerization method.The effects of several reaction conditions including oxidant/monomer molar ratio, polymerization temperature and reac
In order toincrease the electrical conductivity greatly but maintain a large Seebeck coefficient and a low thermal conductivity simultaneously, the binaryphased LaCeFe3CoSb12-Sb nanocomposites compose
目前使用的氮化物LED一般生长在蓝宝石衬底上.该技术存在几个严峻的问题:一方面,蓝宝石价格昂贵,使得氮化物器件生产成本高昂;另一方面,蓝宝石热导率低,不利于开发高功率氮化物器件;再次,基于蓝宝石上的LED核心技术几乎已全部欧美国家垄断并申请了专利.
会议
A type of PTFE/MoS2/glass fiber composite has been used as bearing cage material.To study the friction properties, the tests have been performed under various parameters on block-on-ring.The experimen
In this letter, Lawson cypress leaf-like ZnO hierarchical nanostructures with new and interesting morphology were synthesized by electrodeposition in aqueoussolution of Zn (NO3)2 followed by annealing
In order to short reduction period, decrease energy consumption and lower labour-intensive in the production of Mg reduction, a kind of vertical and fast reduction Mg furnace was developed to come int
Mesoporous ZnO thin film is an important part of dye-sensitized solar cells (DSSCs) due to it determines the amount of adsorbed dyes.However, small specific surface area of ZnO thin film prepared by o
Facile synthesis of CaCO3 and CaCO3∶Eu3+ phosphors by solid state reaction at room temperature and t
The CaCO3 and CaCO3∶Eu3+ phosphors have been synthesized by solid state reaction at room temperature without further sintering treatment.