【摘 要】
：
In this study,Al matrix nanocomposites containing 1,2 and 4 wt％ nano-boron nitride were fabricated by mechanical milling and hot extrusion.The mechanical properties of all extruded samples were evaluated.Also,the morphology and microstructure of the mille
【机 构】
：
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, I
论文部分内容阅读
In this study,Al matrix nanocomposites containing 1,2 and 4 wt％ nano-boron nitride were fabricated by mechanical milling and hot extrusion.The mechanical properties of all extruded samples were evaluated.Also,the morphology and microstructure of the milled composite powders were characterized using two types of electron microscope.The results showed that a high fraction of the boron nitride nanoparticles dissolved and formed a solid solution in Al matrix during the milling process.Through the process of solid solution formation,the work hardening rate of the composite powders increased.This led to a morphological change in the composite powders and resulted in equiaxed shape.The powder particle size also decreased after the milling process.By increasing boron nitride content within a range of 0-4 wt％ in the hot extruded samples,tensile stress increased from 212 to 333 MPa.The hardness of the nanocomposite samples including 1,2 and 4 wt％ boron nitride improved approximately 55,70 and 90％ in comparison with pure Al,respectively.
其他文献
The fracture of pipelines caused by corrosion cracks and the resulting oil and gas leakage can lead to great environmental pollution and economic losses.These negative effects are due to serious corrosion of the plain carbon steels used for armor of flexi
The strain rate sensitivity (SRS) and temperature sensitivity (TS) of 316L austenitic stainless steel were investigated by constant strain rate test (CSRT) and strain rate jump test (SRJT) under four temperatures (293,373,473 and 573 K) and four strain ra
Three-dimensional parts of the 30CrMnSiA steel were successfully fabricated using selective laser melting (SLM).The microstructures and mechanical properties of the SLM-processed 30CrMnSiA samples were investigated by scanning electron microscope and tran
The crevice corrosion behaviors of 436 stainless steels in chloride-containing solutions with sulfate addition were studied using potentiodynamic,galvanostatic and repassivation potential measurements.The results of these electrochemical tests were compar
The hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 ℃ and strain rates of 0.01-10 s-1.The effects of Cu addition and different deformation parameters on defo
In this study,series of nanolayered structures of Zn-Al LDHs were prepared by urea hydrolysis.Nanofibers and nanonets of the Al-doped ZnO were formed via the decomposition of the nanolayers under high pressure and temperature.Nanospheres were also prepare
A356-carbon nanofibers (CNFs) composites with different contents of CNFs were fabricated by ultrasonic vibration casting to investigate the effect of CNFs in the matrix on the mechanical properties and wear resistance.The worn surfaces were investigated u
In this work,the influence of pulse current parameters on springback and bending force of magnesium alloy during electropulse-assisted (EPA) V-bending was investigated.The experimental results showed that pulse current can effectively reduce the springbac
The unique phase transformation and carbide evolution in 9Cr18 steel were investigated during semi-solid forming and subsequent heat treatment.The functional gradient thixoforging 9Cr18 component was divided into inner area and edge area.Microstructure ev
This study examines the relationship among cooling rate,microstructure and mechanical properties of a sand-casted A1-5.0Mg--0.6Mn-0.25Ce (wt％) alloy subjected to T4 heat treatment (430 ℃ × 12 h + natural aging for 5 days),and the tested alloys with wall t