Red Cement-based Decorative Mortar Prepared with Dry Electroplating Sludge Containing Pb as Red Pigm
【机 构】
:
Key Laboratory of Advanced Civil Engineering Materials Ministry of Education, Tongji University, Sha
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2014年2期
其他文献
The aim of this study was to improve the cyclic oxidation resistance of In718 superalloy by laser peening(LP). Specimens were treated by LP from one to three times, respectively. The cyclic oxidation tests at 900℃ for periods up to 2 h were conducted. Cha
The degradation mechanisms of cementitious materials exposed to sulfate solutions have been controversial, despite considerable research. In this paper, two methodologies of image analysis based on scanning electron microscope and chemical mapping are use
The dynamic observations of bainitic transformation in a Fe-C-Mn-Si superbainite steel were conducted on a high temperature laser scanning confocal microscope. It is indicated that the mutual intersection of bainite sheaves often occurs during growth of b
Preparation and Spectral Analysis of Gold Nanoparticles Using Magnetron Sputtering and Thermal Annea
Gold (Au) nanoparticles were prepared on Au-film-coated K9 glass and silicon substrates by direct current (DC) magnetron sputtering and thermal annealing treatment. The effects of substrate material, annealing temperature, and time on morphologies of Au n
Effects of Mechanical Alloying Parameters on the Microstructures of Nanocrystalline Cu-5 wt% Cr Allo
A new kind of composite buffering material was made by filling the voids of honeycomb paperboard with polyurethane. Drop tests were performed to evaluate the dynamic energy absorption capacity of the material. Based on the tests results, we analyzed the m