在普通的氧化物镀锌溶液中工作,均采用低的电流密度(0.5~2安培/平方公寸)。当采用含有各种光泽形成剂的电镀溶液时,电流密度的采用值大大地提高,并且相应地加快了操作速度。全苏航空材料研究所所配制的电镀溶液,采用了极高的电流密度(达10安培/千方公寸)。H.T.库特里耶夫采夫的操作方法,用压缩空气搅拌电镀溶液,则大大的加速了锌酸監电镀溶液中锌的沉积过程。有一些新的配方,其中一种是在电镀溶液中采用焦磷酸監,它的好处是可以采用高达6安培/平方公寸的电流密度。在酸性镀锌溶液中加入光泽剂,可提高陰极电流密度
In ordinary oxide zinc solution work, are used low current density (0.5 ~ 2 amps / square inch). When plating solutions containing various gloss formers are used, the current densities are greatly increased and the operating speed is correspondingly increased. The electroplating solution prepared by the Institute of Aeronautical Materials of the All-China uses a very high current density (up to 10 amps / square inch). H.T. Kotriyevtsev’s method of operation, using compressed air to agitate the electroplating solution, greatly accelerates the deposition of zinc in the zinc acid electroplating solution. There are some new recipes, one of which is the use of pyrophosphate in electroplating solutions. The advantage is that current densities up to 6 amps / square inch can be used. In acid zinc solution by adding brightener, can improve the cathode current density