【摘 要】
：
采用化学浴沉积法分别将CdS、CdSe量子点沉积在TiO2纳米纤维薄膜上,得到TiO2/CdS/CdSe电极。采用电脉冲沉积法将非晶结构TiO2薄膜插入CdS与CdSe量子点之间,得到TiO2/CdS/a-Ti
【机 构】
：
内蒙古化工职业学院,呼伦贝尔职业技术学院,
论文部分内容阅读
采用化学浴沉积法分别将CdS、CdSe量子点沉积在TiO2纳米纤维薄膜上,得到TiO2/CdS/CdSe电极。采用电脉冲沉积法将非晶结构TiO2薄膜插入CdS与CdSe量子点之间,得到TiO2/CdS/a-TiO2/CdSe电极。将两种电极分别组装成太阳能电池,进行光电化学性质研究,结果表明,TiO2/CdS/a-TiO2/CdSe电池的光电转化效率比TiO2/CdS/CdS电池提高了1.68倍。进一步的原因分析结果表明,在CdS与CdSe量子点之间插入TiO2非晶薄膜后,可以极大提高载流子寿命。
The CdS and CdSe quantum dots were deposited on the TiO2 nanofibers films respectively by chemical bath deposition method to obtain TiO2 / CdS / CdSe electrodes. The TiO2 / CdS / a-TiO2 / CdSe electrode was obtained by inserting the amorphous TiO2 film into the CdS and CdSe QDs by electrical pulse deposition. The results show that the photoelectric conversion efficiency of TiO2 / CdS / a-TiO2 / CdSe battery is 1.68 times higher than that of TiO2 / CdS / CdS battery. Further analysis of the results shows that the intercalation of CdTe and CdSe QDs can greatly improve the carrier lifetime.
其他文献
将苯胺单体引入无烟煤的微纳米孔隙及芳香层片中,原位聚合制备出含微纳米结构特征的无烟煤/聚苯胺复合材料,其电导率稳定在101S·m-1数量级。并分别用SEM、FTIR电阻仪和电化
分别采用碳纳米管(CNTs)和石墨烯对聚酰亚胺树脂进行增强,制备了碳纤维增强复合材料。测试复合材料在不同温度下拉伸、弯曲、层剪等力学性能,通过SEM和TEM对材料微观结构进行
以过硫酸铵(APS)、氯化铁(FC)作为氧化剂,十二烷基苯磺酸为掺杂剂,采用微波化学氧化法合成两种掺杂态的聚苯胺复合材料PANI-DA和PANI-DF,并利用FT-IR、SEM、XRD、TGA和四探针
采用溶胶-凝胶法合成TiO2纳米粉,并分别在500、600和700℃进行煅烧。并以此为前驱物,采用微波水热合成法制备TiO2纳米管。用X射线衍射(XRD)、场发射扫描电镜(FESEM)和场发射
研究了采用聚氨酯(PU)和木粉为原料制备发泡木塑复合材料(FWPC).以木粉质量分数、硅烷偶联剂(KH550)加入量、温度和时间4个因素为条件,分别以压缩强度和密度为考核指标,采用
市场对抗菌纺织品需求越来越大.选用卤胺化合物和季铵盐两种抗菌剂处理棉织物.合成了5,5-二甲基-3-(3'-三乙氧基硅丙基)-海因(DTH)及其聚合物(PDTH),3-(三乙氧基甲硅烷基)丙
采用溶胶-凝胶法在FTO玻璃上制备TiO2介孔薄膜,重点研究了悬涂次数对薄膜的厚度及孔径大小的影响。对所制备的TiO2介孔薄膜进行X射线衍射分析,结果表明结晶度好,为锐钛矿结构
针对芳纶纤维表面光滑、惰性强、与橡胶的黏接性能差,严重影响了橡胶复合材料力学性能的缺点。采用KMnO4(5%)+H2SO4(15%)以1∶1混合溶液和K2Cr2O7(10%)+H2SO4(25%)以1∶1混合
在微波作用下,以膨润土、二氧化钛、氯化铝为原料制备了掺Al-TiO2改性膨润土复合材料,通过扫描电子显微镜(SEM)和X-射线衍射(XRD)等手段对复合材料的形貌和结构进行表征,并考
以羟乙基纤维素(HEC)、正硅酸乙酯(TEOS)为原料,通过溶胶-凝胶法制备了不同TEOS含量的新型有机-无机杂化膜。通过红外(FT-IR)、热重(TG)等分析手段对膜进行了表征,并以不同浓