The microstructure,mechanical properties and corrosion behavior of Mg-2Zn-0.6Zr alloy under the as-cast and asextruded conditions were investigated.Microstructure analysis indicated the remarkable grain refinement by extrusion,as well as notable reduction
【机 构】
：
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 1
论文部分内容阅读
The microstructure,mechanical properties and corrosion behavior of Mg-2Zn-0.6Zr alloy under the as-cast and asextruded conditions were investigated.Microstructure analysis indicated the remarkable grain refinement by extrusion,as well as notable reductions in volume fraction and size of precipitate phases.As compared with the as-cast alloy,the asextruded alloy exhibited better mechanical performance,especially in yield strength which was promoted from 51 to 194 MPa.Refined grains,dispersive precipitate phases and texture were thought to be the main factors affecting the improved performance in strength.The electrochemical measurement and immersion test revealed the corrosion rate of Mg-2Zn-0.6Zr alloy by extrusion decreased from 1.68 to 0.32 mm/year.The reasons for the enhanced corrosion resistance were mainly attributed to the decreased volume fraction and Volta potential of the precipitate phases,the refinement of the grain size,as well as the formation of more protective corrosion film.
其他文献
Ti-Ta alloys have been widely studied for biomedical applications due to their high biocompatibility and corrosion resistance.In this work,nearly fully dense and in situ alloyed Ti-50 wt％ Ta samples were fabricated by the laser powder bed fusion (LPBF) of
The effect of stacking fault energy (SFE) on the grain structure evolution of face-centered cubic metals during friction stir welding was investigated by using pure aluminum,pure copper and Cu-30Zn alloy as experiment materials.Tool “stop action” and rapi
The NiTi cladding with/without Ni interlayer was prepared on stainless steel (SS) by tungsten inert gas (TIG) surfacing process,aiming at achieving good cavitation erosion resistance.The ranking according to the cavitation erosion resistance is NiTi plate
A systematic study on the wettability and interactions between superalloy melts with various Re contents and Al2O3-based ceramic moulds was presented in this paper.It was found that the increase of Re content inhibited the interfacial reactions to some ex
The microstructure and fracture toughness of weld metal under Ti-free and Ti-containing different fluxes were investigated in this study.It was found that the trace element Ti of flux in submerged arc welding produced significant influence on the fracture
Optimization of grain boundary engineering (GBE) process is explored in a Fe-20Cr-19Mn-2Mo-0.82 N high-nitrogen and nickel-free austenitic stainless steel,and its intergranular corrosion (IGC) property after GBE treatment is experimentally evaluated.The p
The inclination angle of the flake particle has a significant impact on the in-plane thermal conductivity of composites.The graphite flake/Al composites (50 vol％) with different inclination angles were fabricated via flake powder metallurgy,and the result
High-strength,corrosion-resistant,and lightweight Al-Mg alloys perform an important function in harsh coastal service environments.Corrosion resistance is generally inversely correlated with strength;hence,it is difficult to simultaneously optimize both.I
Ni-Mo-P coatings are obtained at the surface of ceramic substrate by electroless deposition using palladium as a surface catalyst.The influence of catalyst activation conditions on coatings\' properties was assessed by structural,morphological,electrica
Mg and its alloys are the lightest structural metals available and are extremely attractive for applications as lightweight components,particularly in the automobile,electronic,and aerospace industries.The global market for wrought Mg alloys has steadily