【摘 要】
：
This study investigates the bulk density, sintering behaviour, and microwave dielectric properties of the MgO–2B2O3 series ceramics synthesised by solid-state reaction. According to the X-ray diffraction and microstructural analyses, the as-prepared MgO–2
【机 构】
：
Collaborative Innovation Center for Exploration of Hidden Nonferrous Metal Deposits and Development
论文部分内容阅读
This study investigates the bulk density, sintering behaviour, and microwave dielectric properties of the MgO–2B2O3 series ceramics synthesised by solid-state reaction. According to the X-ray diffraction and microstructural analyses, the as-prepared MgO–2B2O3 ceramics possess a single-phase structure with a rod-like morphology. The effects of different quantities of H3BO3 and BaCu(B2O5) (BCB) on the bulk density, sintering behaviour, and microwave dielectric properties of the MgO–2B2O3 ceramics were investigated. Accordingly, the optimal sintering temperature was obtained by adding 30 wt％ H3BO3 and 8 wt％ BCB. We also reduced the sintering temperature to 825℃ . Furthermore, the addition of 40 wt％ H3BO3 and 4 wt％ BCB increased the quality factor, permittivity, and temperature coefficient of resonance frequency of MgO–2B2O3 to 44,306 GHz (at 15℃GHz), 5.1, and?32 ppm/, respectively. These properties make MgO–2B2O3 a viable low- temperature co-fired ceramic with broad applications in microwave dielectrics.
其他文献
根据事故致因理论,人的不安全行为属于引发各类生产安全事故的直接原因.改善人的行为方式,减少人的不安全行为是企业安全生产工作的重中之重.本文主要通过对某天然气净化厂2016-2020年统计的人的不安全行为进行分类、分析,深度研究问题产生根源,制定管理改进对策,完善安全管理措施,探讨如何提高发现问题的利用效率,提升企业安全管理水平.
选择密封常用的丁腈橡胶材料,以O形圈静密封结构为例,采用压缩永久变形法在空气和液压油中进行材料性能退化试验,得到性能退化模型,并计算密封结构在不同环境中的寿命.结果 表明,采用压缩永久变形法进行O形圈静密封结构寿命预测可节约大量时间和工作成本,寿命预测准确性较高.
研究3×0.22/9×0.20CCUT特高强度钢丝帘线的性能及其替代3×0.24/9×0.225CCHT高强度钢丝帘线在12R22.5挂车专用无内胎全钢载重子午线轮胎胎体中的应用.结果 表明,与3×0.24/9×0.225CCHT钢丝帘线相比,3×0.22/9×0.20CCUT钢丝帘线的直径和线密度较小,最小破断力略高,可以减小压延厚度和密度,降低压延工艺损耗,在保证轮胎综合使用性能的同时,促进轮胎轻量化,降低生产成本.
研究超耐磨炭黑Vulcan 9HX1在全钢载重子午线轮胎胎面胶中的应用.结果 表明,胎面胶采用90份天然橡胶、10份顺丁橡胶的生胶体系,选用超耐磨炭黑Vulcan 9HX1替代炭黑N134进行补强,硫化胶老化前后耐磨性能有较大幅度提高,定伸应力和撕裂强度均有所提高,压缩疲劳温升和损耗因子明显降低,成品轮胎室内试验行驶里程长.经过40 d的路试,轮胎平均单位磨耗行驶里程达到26000 km·mm-1,轮胎使用寿命延长.
研究环保型塑解剂A86在半钢子午线轮胎胎体胶中的应用.结果 表明:在以天然橡胶为主的半钢子午线轮胎胎体胶中添加塑解剂A86,胶料的门尼粘度大幅降低,焦烧时间延长,加工性能改善;硫化胶的定伸应力和钢丝粘合力提高;成品轮胎的强度性能、耐久性能和高速性能均达到企业标准要求.
The growing demand for high-power-density electric and electronic systems has encouraged the development of energy-storage capacitors with attributes such as high energy density, high capacitance density, high voltage and frequency, low weight, high-tempe
不溶性硫黄Crystex Cure Pro(简称Cure Pro)具有高分散性、高热稳定性、高含量等特点.在全钢子午线轮胎中使用Cure Pro替代不溶性硫黄HDOT20可减少胶料的喷霜,提高胶料与钢丝的粘合性能.同时因Cure Pro的有效硫含量较高,其在配方中的用量可减小,性价比较高.
介绍影响全钢载重子午线轮胎成品室内试验数据准确性的主要因素,结合试验设备精度的标定和试验方法的调整等,提出相应的改进措施,可以提升全钢载重子午线轮胎成品室内试验数据的准确性和轮胎行驶的安全性.
研究不同种类粘合树脂对轮胎带束层胶料性能的影响.结果 表明:新型粘合树脂MPRF,PRF和MPF游离单体含量低,在胶料加工过程中不产生刺激性气味,不冒烟,环保;与添加普通粘合树脂SRF的胶料相比,添加新型粘合树脂MPRF,PRF和MPF的胶料FL和Fmax较低,抗硫化返原性相对较好,门尼焦烧时间较长,胶料加工安全性提高;硫化胶的拉伸强度和拉断伸长率较高;钢丝帘线H抽出力在1000 N以上,完全能满足带束层对钢丝帘线粘合性能的要求.
通过控制胎面挤出过程,调整基部胶厚度占胎面总厚度的比例(以下简称基部胶厚度占比,分别取20％,35％和50％),研究胎面基部胶厚度占比对轮胎性能的影响.结果 表明,适当增大基部胶厚度占比可以提高轮胎的耐久性能,减小轮胎过坎冲击力,提高乘坐舒适性,增大侧向力,提高操纵性能,增大纵向力和接地面积,提高抓着性能和制动性能,并且降低滚动阻力系数,提高燃油经济性.