Effects of Deformation Texture and Twins on the Corrosion Resistance of Rolled AZ31 Mg Alloy Under 5
【出 处】
:
金属学报(英文版)
【发表日期】
:
0年期
其他文献
The influence of asymmetric reduction rolling (ARR) on the microstructure,texture and mechanical properties of AZ91 was investigated.The microstructural characteristics of the AZ91 sheet processed by symmetric rolling (SR) were the twins,intersection of t
Young\'s modulus is a critical parameter for designing lightweight structure,but Al and its alloys only demonstrate a limited value of 70-72 GPa.The introduction of carbon nanotubes (CNTs) is an effective way to make Al and its alloys stiffer.However,li
Effect of Phase Transformation During Long-Term Solution Treatment on Microstructure, Mechanical Pro
The influence of long-term solution treatment for various intervals on the microstructure, mechanical properties, and corrosion resistance of the as-cast Mg-5Zn-1. 5Y alloy was investigated. Variation of secondary phases was studied during solution treatm
Corrosion resistance behavior of Co-containing maraging stainless steels was investigated.Neutral salt spray and polarization test showed that maraging stainless steel with high Co content showed poor corrosion behavior.Microstructure observation proved t
Pulsed external field,including electric,magnetic,ultrasonic and laser,as an instantaneous high energy input method with high efficiency and low energy consumption,have long been known to can modify the microstructure and properties of materials.This incl
期刊
Phase Structure and Electrochemical Properties of Melt-Spun La4MgNi17.5Mn1.5 Hydrogen Storage Alloys
The (La4MgNi17.5Mn1.5) alloys at different melt-spun speeds were prepared by using a vacuum melt-spun furnace,and the phase structure and electrochemical properties of alloys were studied.X-ray diffraction analysis results show that melt-spun La4MgNi17.5M
Effect of Al4C3 Particle Size Distribution in a Al-2.5C Master Alloy on the Refining Efficiency of t
The Al-2.5C master alloy is prepared to investigate the effect of the Al4C3 particle size distribution on the refining efficiency of the AZ31 alloy.The results indicate that the Al4C3 particles are potent nucleation substrates for primary α-Mg grains.With
The present work focuses on the structural stability upon hydrogenation of three typical La-Mg-Ni-based alloys: La2-MgNi9, La3MgNi14 and La4MgNi19. Structural changes during gaseous and electrochemical cycles were characterized, and the influence of the s
Open-celled porous (TiB2-Al2O3)/NiAl composites were successfully fabricated by using spherical carbamide as space holders via self-propagating high-temperature synthesis (SHS).Effects of 10Al-3B2O3-3TiO2 contents (0-20 wt%) on the pore structures and the