【摘 要】
：
本文重点讨论了分阶段时效处理对Nb-46.5(wt)%Ti合金的临界电流密度(Jc)的影响。经过试验,确定了较为合理的时效次数、时效参数(温度与保温时间)、附加形变量等,并与一次性时
论文部分内容阅读
本文重点讨论了分阶段时效处理对Nb-46.5(wt)%Ti合金的临界电流密度(Jc)的影响。经过试验,确定了较为合理的时效次数、时效参数(温度与保温时间)、附加形变量等,并与一次性时效处理进行了对比。对晶界的钉扎作用与提高高场下Jc的途经提出了初步看法。经试验Nb-46.5(wt)%Ti合金的Jc值己达2.677×10~5A/cm~2(5T,4.2K),最高可达3.06×10~5A/cm~2。
This article focuses on the effect of staged aging on the critical current density (Jc) of Nb-46.5 (wt)% Ti alloys. After testing, the more reasonable number of aging, aging parameters (temperature and holding time), additional deformation, etc. were determined, and compared with the one-time aging treatment. A preliminary view on the pinning effect on the grain boundaries and the way to improve Jc at high field was proposed. The Jc value of the tested Nb-46.5 wt% Ti alloy reached 2.677 × 10 -5 A / cm 2 (5T, 4.2 K) and the maximum value was 3.06 × 10 -5 A / cm 2.
其他文献
---目…期…页}题目…期…18 1222529141 21 1 510幻29qU决Uj.二舀.二八Ot‘勺‘丹」1619228 27 323438342 工b,占‘.三8内」ZC‘21了.,占一匕月‘.上,二.二心‘2口.三。目一
武汉钢铁公司冷轧厂1700镀锌机组是由西德引进的成套设备。为保证镀层均匀,该机组采用吹镀法,机组上设有吹气装置。该装置为德马克公司的专利。对装置上的喷口曲线,国内现采
A. Comparisons With 1958 1. Gross domestic product (GDP) :2.452 billion yuan ($360 million) in 1958; 595.6 billion
A. Comparisons With 1958 1. Gross domestic p
带金属骨架的橡胶制品是用模压法在平板硫化机上硫化成型的,(图1)。由于金属骨架包在橡胶内部,在模具型腔内无法定位,所以,当模具在压力作用下闭合时,金属骨架便在热熔橡胶
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
这种夹头,主要用在攻丝和铰孔时,装夹丝锥和铰刀之用,可增加刃具的使用寿命、减少生产的辅助时间和提高工作效率。其结构如图所示。在锥形尾柄1的头部筒壁间装有三个传递扭
一九八二年九月十九日至二十日,由中国船舶工业总公司和河南省国防工办主持在河南柴油机厂举行铝硅合金810锶盐长效变质剂鉴定会。南京工学院、吉林工业大学、郑州工学
Fro
为了在2B440A型座标镗床上精加工9XC和X12φ1钢(硬度为HRC58～64)制的模具零件上的阶梯孔,应用了超硬材料ИK—1(苏联牌号)制的刀具。其几何角度为:主偏角φ=45°,付偏角φ1=1
最近,温州电讯厂试制成功一种液晶自动护目镜片所配置的面罩。该液晶自动护目面罩是利用液晶光阀的特殊电光特性,配有光电装置和光学滤色镜等能自动迅速遮挡强烈光线。当焊