Numerical Simulation and Experimental Research on Penetration of Composite Ceramic Armor by Rod Proj
【机 构】
：
The Ningbo Branch of Ordnance Science Institute of China,Yantai 26400,China;Hainan Second Metallurgy
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
【发表日期】
：
2010年6期
其他文献
Microstructure and Mechanical Properties of Ultrafine Grained Mg15Al Alloy Processed by Equal-channe
Formation,solution and phase change of hydration products in MgO-MgCl_2-H_2O system was studied with thermodynamics method,and resistance to water immersion and phase change of magnesium oxychloride cement with different MgO/MgCl_2 molar ratio was experim
Mechanical and Thermal Properties of Muscovite and Density Polyethylene-reinforced and-toughened Pol
The mechanical and thermal properties of polypropylene(PP)/muscovite/ low-density polyethylene(LDPE)/polypropylenegraftmaleic anhydride(PP-g-MAH)ternary com-posites were investigated.In PP matrix,muscovite,LDPE,and PP-g-MAH were added as strength-ening ag
Six kinds of polyurethane(PU)elastomers were prepared based on different poly-esters,polyethers and chain extenders.The structure,mechanical properties and cold resistant proper-ties of PU were systematically investigated by FTIR,XRD,DMTA,universal testin
The Al-Ca-Ba glass system with good chemical durability was firstly investigated as the scintillators host.Luminescence properties of Ce~(3+)ions in this glass were studied,and obvious red shift and larger stokes shift with respect to others system were i
A Comparative Study of Tribological Properties between Perfluoro and Non-perfluoro Alkylsilane Self-
The tribological properties of perfluoro and non-perfluoro alkylsilane molecular films were investigated and compared detailedly.Their surface properties were characterized by X-ray photoelectron spectroscopy(XPS),atomic force microscopy(AFM)and contact a
The microstructure with uniform equiaxed fine gain was obtained by the thermo-mechanical processing(TMP)for the 5083 Al alloy(Al-4.56%Mg-0.61%Mn)plate.Uniaxial tensile test was carried out at a temperature range of 500-570℃and a strain rate range of 4.17×
Effeet of Intermediate Heat Treatment Temperature on Microstructure and Notch Sensitivity of Laser S
The properties and microstructure of microwave and conventional sinteredFe-2Cu-0.6C powder metallurgy (PM) alloys were investigated. The experimental results show that microwave sintered alloy has the better properties (sintered density 7.20 g/cm3, Rockwe