The influence of asymmetric reduction rolling (ARR) on the microstructure,texture and mechanical properties of AZ91 was investigated.The microstructural characteristics of the AZ91 sheet processed by symmetric rolling (SR) were the twins,intersection of t
【机 构】
：
School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China;P
论文部分内容阅读
The influence of asymmetric reduction rolling (ARR) on the microstructure,texture and mechanical properties of AZ91 was investigated.The microstructural characteristics of the AZ91 sheet processed by symmetric rolling (SR) were the twins,intersection of twins and dynamic recrystalization (DRX) grains around the coarse grains and within the twins.However,the amount of twins and DRX grains in ARRed AZ91 was much smaller than that in SRed AZ91.The SRed AZ91 after annealing exhibited fine DRX grains and some coarse grains with a size of ～ 100 μtm.The grains in ARRed AZ91 after annealing were much finer and more homogeneous than those in SRed AZ91 after annealing.The intensity of basal texture of ARRed AZ91 after annealing was lower than that of SRed AZ91 rolling after annealing.The average Schmid factor of ARRed AZ91 is 0.34,which is higher than that of SRed AZ91.The yield strength and ultimate tensile strength of the ARRed AZ91 sheet were increased to 16.1％ and 31.8％ compared to SRed AZ91 sheet,from 155 to 180 MPa,and from 220 to 290 MPa,respectively.The improvement of mechanical properties in ARRed AZ91 after annealing was attributed to much finer,more homogeneous DRX grains and weaker basal texture.
其他文献
The defects created in commercial dental alloys during blasting with alumina particles propelled in compressed air under pressure 0.1 and 0.4 MPa have been studied using positron annihilation spectroscopy,scanning electron microscopy and X-ray diffraction
A series of Ti2ZrHf0.5VNbx (x =0,0.25,0.5,0.75 and 1.0) refractory high-entropy alloys were prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties.All the alloys displayed a simple BCC structure.The microstructu
The development of high-entropy alloys (HEAs) has stimulated an ever-increasing interest from both academia and industries.In this work,three novel MoNbFeCrV,MoNbFeCrTi,and MoNbFeVTi HEAs containing low thermal neutron absorption cross section elements we
This paper presents a new thermomechanical model of friction stir welding which is capable of simulating the three major steps of friction stir welding (FSW) process,i.e.,plunge,dwell,and travel stages.A rate-dependent JohnsonCook constitutive model is ch
A calculation method based on a combination of △g parallelism rule,good matching site (GMS) analysis,CSL/DSCL (coincidence site lattice/displacement shift complete lattice) and the O-lattice theory has been applied to interpret the observation of the habi
In pressurized water reactor,fretting corrosion has become the main reason for the failure of 690TT heat exchanger tubes.The effect of temperature on the fretting corrosion behavior between 690TT tube and 405 stainless steel (SS) bar has been studied duri
Mg-3Al-1Zn alloy sheets have been deformed by continuous bending (CB) to investigate the effects of processing parameters (bending angle and repetitive passes) on the texture and formability.The samples exhibited a bimodal microstructure with abnormal gro
The microstructure,texture,residual stress,and tensile properties of Mg-6Zn-2Y-1La-0.5Zr (wt％) magnesium alloy were investigated before and after extrusion process,which performed at 300 ℃ and 400 ℃.The microstructural characterizations indicated that the
A modified strain-induced melt activation (SIMA) process consisting of homogenization,equal-channel angular pressing (ECAP) and subsequent heating to the semisolid temperatures was introduced to prepare the 7075 aluminum alloy with superior thixotropic be
The variant selection of martensites (ε-M and α\'-M) and ε-M reversion in dynamic tensile high-manganese TRIP steel were investigated.α\'-M variant pairs with a zigzag morphology frequently formed,and the pairs of neighboring α\'-M variants were exa