【摘 要】
：
The key point in CO2 methanation is to improve the activity at low temperature and the stability.For this purpose,a new cerium-modified Ni-La2O3/ZrO2 catalyst was prepared using La1-xCexNiO3/ZrO2 with perovskite phase as the precursor,which was obtained b
【机 构】
：
Department of Catalysis Science and Technology, School of Chemical Engineering, Tianjin University,
论文部分内容阅读
The key point in CO2 methanation is to improve the activity at low temperature and the stability.For this purpose,a new cerium-modified Ni-La2O3/ZrO2 catalyst was prepared using La1-xCexNiO3/ZrO2 with perovskite phase as the precursor,which was obtained by citrate complexation combined with an impregnation method.The resulting catalyst was characterized through Nitrogen adsorption and desorption,X-ray diffraction (XRD),Transmission electron microscopy (TEM),Hydrogen temperature programmed re duction (H2-TPR),Temperature-programmed desorption of CO2 (CO2-TPD) and that of H2 (H2-TPD),andX-ray photoelectron spectroscopy (XPS) techniques,and the catalytic performances for CO2 methanation was investigated.Cerium modification could improve the effective activation of CO2,thus enhancing the activity at low temperature for CO2 methanation.The metal Ni nanoparticles prepared using this method were highly dispersed and showed excellent resistance to sintedng,leading to very good stability,which could be attributed to the following:Ni nanoparticles could be confined by cerium-modified La2O3;La2O3 could be confined by the cerium ions at the La2O3/ZrO2 interface;and the cerium ions were confined by ZrO2.
其他文献
A facile hydrolysis method was applied to fabricate high-performance Co-layered double hydroxide (LDH) nanocages/graphene composites for supercapacitors.The materials exhibit enhanced rate capability than the counterpart electrode free of graphene while m
We have studied the redox potentials and electronic properties of C60 and C59N using density functional theory method.It is found that doping C60 with one nitrogen atom results in a slight increase in redox potential.Next,we have also studied C59N functio
Herein,we report visible light active mesoporous cadmium bismuth niobate (CBN) nanospheres as a photocatalyst for hydrogen (H2) generation from copious hydrogen sulfide (H2S).CBN has been synthesized by solid state reaction (SSR) and also using combustion
Herein,we reported in situ synthesis of biomass-derived Ni/C catalyst by self-reduction with pomelo peel.Compared with the conventional method,which includes carbonization,activation,impregnation and reduction,the entire preparation process was simplified
Cux-Fey/SiO2 catalysts were prepared using urea-assisted sol-gel method.The structure and physicochemical properties of the catalysts were characterized using N2 adsorption-desorption,transmission electron microscopy,H2-temperature-programmed reduction,po
The capacity to capture CO2 was determined in several stoichiometric compositions in the Li2O-Bi2O3 system.The compounds (Li7BiO6,Li5BiOs,Li3BiO4 and LiBiO2 phases) were synthesized via solid-state reaction and characterized by X-ray diffraction,scanning
High-quality graphene flakes have long been desirable for numerous applications including energy storage,printable electronics,and catalysis.In this contribution,we report a green,efficient,facile gas-driven exfoliation process for the preparation of high