Hexagonal boron nitride (h-BN) fillers are incorporated into poly(vinyl butyral) (PVB) coatings to improve the corrosion protection performance of copper.It has been revealed that the h-BN fillers exhibit an ex-cellent dispersiblility in PVB coating due t
【机 构】
：
CAS Key Laboratory of Marine Environmental Corrosion and Bio-fouling,Institute of Oceanology,Chinese
论文部分内容阅读
Hexagonal boron nitride (h-BN) fillers are incorporated into poly(vinyl butyral) (PVB) coatings to improve the corrosion protection performance of copper.It has been revealed that the h-BN fillers exhibit an ex-cellent dispersiblility in PVB coating due to the non-covalent interactions between h-BN fillers and the PVB molecules.Electrochemical characterization reveals that the corrosion resistance of the BN-reinforced PVB (BN-P) coating is 5-6 orders of magnitude higher than that of the pristine PVB coating.Photographs and metallography show that the copper substrate beneath the BN-P coating does not suffer from corro-sion after immersion for 2 months,indicating that the BN-P coating can provide a long-term protective barrier for the underlying copper substrate.Loading 0-0.25 g h-BN fillers in 2.0 g PVB,the corrosion pro-tection performance increases with increasing the loading of h-BN fillers.The scratch test results suggest that h-BN fillers do not accelerate copper corrosion when the BN-P coating is damaged.
其他文献
根据上海地区不同土层软土的一维和等向固结试验,得到一维固结下压缩指数Cc和回弹指数Cs与修正剑桥模型参数λ和κ之间的关系.鉴于室内试验耗时过长,而通过土样的基本物理指标(天然含水率wn、孔隙比e0、液限wL和塑性指数Ip)来推算压缩指数和回弹指数是一个快捷有效的方式,对比发现土的变形指标与基本物理指标间存在一定的相关性.结果表明:Cc/n0与Cc,Cs′/n0与三轴试验各向同性固结下得到的Cs′之间存在较好的线性关系,并给出了对应的关系式.由此,上海地区软土的变形指标可通过初始孔隙率来估算.在已有试验数据
针对三维数值流形法中罚函数法施加任意方向边界位移和多步加载误差累积问题,通过修正传统三维数值流形法控制方程中的位移边界部分,推导出含沿着某一方向施加边界位移条件和相应的分步加载情况的计算公式,以期扩大控制方程在位移边界处理上的适用范围和减少多步加载误差累积效应.选取2个典型算例进行数值模拟和对比分析,验证该方法的准确性.计算结果表明:文中方法的计算结果与解析解相吻合,修正公式适用于不同方向施加边界位移的情况,具有较强的适应性;考虑位移边界误差修正比不考虑误差修正的计算精度高;随分步加载步数的增多,不考虑位
闸站基坑开挖过程中的降水问题重要且复杂.采用“大井法”和数值模拟2种方法,对引江济淮工程中凤凰颈泵站改造的基坑涌水量进行了计算.基于三维渗流模型对基坑降水方案作了优化研究,对比分析了降水井的空间布置和井深度变化对基坑降水效果的影响,并综合考虑了工程经济性和施工便捷性,最终得到了推荐的降水方案.通过对各降水方案的分析可知:在基坑降水满足降深要求的前提下,降水井空间分布越均匀,各井抽水量的差距越小,有利于统一的水泵配购;将降水井布置在基坑周边,避免在基坑内部布井,能够减小对施工的干扰,但会显著提高总抽水量;降
为揭示深埋大理岩在不同应力路径下的变形特征和能量演化特征,基于大理岩的常规三轴试验和卸荷三轴试验,分析了大理岩变形破坏过程中变形和能量演化的围压效应和应力路径影响.结果表明:大理岩在加卸荷条件下均表现出显著的围压效应;卸荷条件下大理岩的损伤扩容应力阈值和峰值强度较加载条件下的低;加载应力路径下能量耗散阶段占比更大,卸荷应力路径下能量聚集阶段占比更大;加卸荷条件下损伤扩容点对应的总能量和弹性应变能与围压具有良好的线性关系;针对峰值应力对应的总能量、弹性应变能及耗散能,加载应力路径下其均与围压具有正线性关系,
中国北方冻土地区的灌区渠道多采用衬砌或者保温措施进行防渗抗冻胀,从而减少输水损失.依据近年来北方冻土地区常用的渠道衬砌形式,从取材和施工的难易程度等角度,对北方高寒地区新疆阿勒泰灌区农十师渠道3种抗冻胀措施的效果进行了研究,分别建立了混凝土、HAS固化剂固化粉煤灰和聚苯乙烯泡沫板(EPS)3种衬砌材料的本构模型.通过ABAQUS温度-应力耦合模拟,分析了3种抗冻胀措施的效果.分析结果表明:3种抗冻胀措施均能有效减少渠道冻胀变形,而HAS固化剂固化粉煤灰和铺设聚苯乙烯泡沫板削减冻胀变形效果更为显著;其中铺设
The microscopic Bouligand-type architectures of fish scales demonstrate a notable efficiency in enhancing the damage tolerance of materials;nevertheless,it is challenging to reproduce in metals.Here bioinspired tungsten-copper composites with different Bo
预应力锚杆因出色的维稳能力及巨大的经济效益,在岩土锚固工程中扮演着重要角色.然而,预应力锚杆的长期性能常因周围恶劣岩土环境的腐蚀而不断退化.为了探究预应力锚杆在模拟岩土环境中的锈蚀机制,通过开展室内加速腐蚀试验,基于电化学阻抗谱及电化学极化曲线分析了处于弱酸、通氧条件下的预应力锚杆腐蚀损伤时变行为,以及该环境下预应力锚杆锚固力与腐蚀速率的关系.结果发现,试验过程中预应力锚杆均未出现明显钝化,浸泡前期处于未通氧环境下预应力锚杆的电化学阻抗谱为一半径很大的容抗弧,预应力锚杆腐蚀不明显,锈蚀受电荷传递控制,中后
随着水利信息化的发展,长江科学院持续加强信息化建设,给水利科学研究和科研管理带来极大的便利;但信息化带来便捷的同时,安全问题也开始逐渐显现.深入分析网络中的各个薄弱环节,提高整体网络安全性,避免发生网络安全事件已成为工作的重点.基于长江科学院的实际网络及业务情况,围绕长江科学院网络安全建设的内容进行探讨,从网络边界、内部网络、内部态势感知3个方面详细分析了长江科学院在目前网络环境下面临的安全风险;并从边界防护、终端防护、服务器防护、态势感知4个方面提出应对策略,阐述了可实施的网络安全技术路线.
为实现WaSSI-C(Water Supply Stress Index-C)模型地理信息系统(GIS)可视化模拟系统,为区域水碳资源分析和模拟决策提供模型工具,在解析WaSSI-C模型理论框架和运行机理的基础上,对模型计算过程进行模块化分解和结构化设计;采用C/S模式构建软件体系架构,基于时空数据模型设计E-R模型图,并应用Geodatabase空间数据库与SQLite关系型数据库联合管理模型参数和时空数据;在.Net开发环境下,基于ArcGIS Engine二次开发组件,使用C#语言进行Scilab.
Detailed three-dimensional (3D) microtomography characterizations of inclusions in electrode matrix,mushy zone (MZ) and liquid melt film (LMF) were performed to elucidate the motion and removal behav-ior of inclusions in electrode tip during magnetically