Several researches have been reported about the characteristic of β-Ga_2O_3 nanowires which was synthesized on nickel oxide particle.But indeed,recent researches about synthesis of β-Ga_2O_3 nanowires on oxide-assisted transition metal are limited to nickel or cobalt oxide catalyst.In this work,Gallium oxide(β-Ga_2O_3)nanowires were synthesized by a simple thermal evaporation method from gallium powder in the range of 700-1000℃ using the iron,nickel,copper,cobalt and zinc oxide as a catalyst,respectively.The β-Ga_2O_3 nanowires with single crystalline without defects were successfully synthesized at the reaction temperature of 850,900 and 950℃ in all the catalysts.But optimum experimental condition in synthesis of nanowires varied with the kind of catalyst.As increasing synthesis temperature,the morphology of gallium oxide nanowires changed from nanowires to nanorods,and its diameter increased.From these results,we could be proposed that the growth mechanism of β-Ga_2O_3 nanowires was changed with synthesis temperature of nanowires.Microstructure and morphology of Synthesized nanowire was characterized by HR-TEM,FE-SEM,EDX and XRD.
Several researches have been reported about the characteristic of β-Ga 2 O 3 nanowires which was synthesized on nickel oxide particle. But indeed, recent researches about synthesis of β-Ga 2 O 3 nanowires on oxide-assisted transition metals are limited to nickel or cobalt oxide catalyst. This work, Gallium oxide (β-Ga_2O_3) nanowires were synthesized by a simple thermal evaporation method from gallium powder in the range of 700-1000 ° C using the iron, nickel, copper, cobalt and zinc oxide as a catalyst, respectively. β- Ga 2 O 3 nanowires with single crystalline without defects were successfully synthesized at the reaction temperature of 850,900 and 950 ° C in all the catalysts. But optimum experimental condition in synthesis of nanowires varied with the kind of catalyst. Ascending synthesis temperature, the morphology of gallium oxide nanowires changed from nanowires to nanorods, and its diameter increased. These results, we could be proposed that the growth mechanism of β-Ga 2 O 3 nanow ires was changed with synthesis temperature of nanowires. Microstructure and morphology of Synthesized nanowire was characterized by HR-TEM, FE-SEM, EDX and XRD.