By using waste bricks as aggregate,a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecological concrete were investigated,and influences of the water-cement ratio,the aggregate-cement ratio and the aggregate size on compressive strength and porosity of the porous ecological concrete were also discussed. Results show that for preparation of the porous ecological concrete,the aggregates should be enveloped with neat cement paste,and recommended fluidity of the cement paste is 200～235 mm. With the increasing of the aggregate-cement ratio,porosity of the porous ecological concrete increases while the 28 d compressive strength decreases. With increasing of the water-cement ratio,porosity of the porous ecological concrete decreases. And relationship between compressive strength and water-cement ratio of the porous ecological concrete does not follow Bolomey’s formula. As a result of this study the porous ecological concrete is prepared,its porosity is 38.93%,the water absorption is 11.39% and the compressive strength is 1.14 MPa. By using waste bricks as aggregate, a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecological concrete were investigated, and influences of the water-cement ratio, the aggregate-cement ratio and the aggregate size on compressive strength and porosity of the porous ecological concrete were also discussed. Results show that for the preparation of the porous ecological concrete, the aggregates should be enveloped with neat cement paste, and recommended fluidity of the cement With the increasing of the aggregate-cement ratio, porosity of the porous wet- tric concrete increases. relationship between compressive strength and water-cement ratio of the porous ecological concrete does not follow Bolomey’s formula As a result of this study the porous ecological concrete is prepared, its porosity is 38.93%, the water absorption is 11.39% and the compressive strength is 1.14 MPa.