【摘 要】
：
A facile scalable synthesis of hierarchical Sb/C micro-/nanohybrid has been addressed in this work, which possesses the advantages of both micrometer and nanometer scale structures as lithium-ion battery anode. Difunctional methacrylate monomers are used
【机 构】
：
North University of China, Taiyuan 030051, China;Ningbo Institute of Materials Technology and Engine
论文部分内容阅读
A facile scalable synthesis of hierarchical Sb/C micro-/nanohybrid has been addressed in this work, which possesses the advantages of both micrometer and nanometer scale structures as lithium-ion battery anode. Difunctional methacrylate monomers are used as solvent and carbon source as well. Liquid precursor of antimony (III) n-butoxide is dissolved in the resin monomer solution, and further incorporated into the cross-linking polymer network via photo polymerization. Through calcination in argon/hydrogen atmosphere, antimony nanoparticles are in situ formed by carbothermal reduction, and homogeneously embedded in the in situ formed micrometer sized carbon matrix. The morphology, structure, crystallinity, spatial dispersion, composition, and electrochemical performance of the Sb/C micro-/nanohybrid are systematically investigated. The cyclic and rate performance of the Sb/C micro-/nanohybrid anode have been effectively improved compared to the pure carbon anode. A reversible capacity of 362 mAh g-1 is achieved with a reasonable mass loading density after 300 cycles at 66 mA g-1, corresponding to capacity retention of 79％. With reducing mass loading density, the reversible capacity reaches 793 mAh g-1 after 100 cycles. Moreover, the electrochemical performance of Sb/C micro-/nanohybrid as sodium-ion battery anode is also investigated in this study.
其他文献
The unique phase transformation and carbide evolution in 9Cr18 steel were investigated during semi-solid forming and subsequent heat treatment.The functional gradient thixoforging 9Cr18 component was divided into inner area and edge area.Microstructure ev
This study examines the relationship among cooling rate,microstructure and mechanical properties of a sand-casted A1-5.0Mg--0.6Mn-0.25Ce (wt％) alloy subjected to T4 heat treatment (430 ℃ × 12 h + natural aging for 5 days),and the tested alloys with wall t
In this study,Al matrix nanocomposites containing 1,2 and 4 wt％ nano-boron nitride were fabricated by mechanical milling and hot extrusion.The mechanical properties of all extruded samples were evaluated.Also,the morphology and microstructure of the mille
The GH4169 superalloy with different content of δ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone (HAZ) was performed in both as-welded and aged state.The results show that the pre
Experiments were carried out to investigate the corrosion behavior of epoxy-coated rebar (ECR) with pinhole defect (diameter in hundreds of microns) immersed in the uncarbonated/carbonated simulated pore solution (SPS) of seawater concrete.Corrosion behav
By using a novel surface modification technique named ultrasonic-electropulsing coupling rolling (UECR) process on an A1-Si casting alloy rod,the surface of material was smoothened significantly.Meanwhile,a strengthened layer with a gradient change in har
This paper reports TiC-(Ni-Cr) metal ceramic alloy (ratio of components 50∶50) with nanoscaled components formed in the surface layer and smoothly transformed into the initial inner structure throughout the material under pulsed electron irradiation of th
In this work,(1-x)CdO-xSnO2 nanocomposites (≤ 0.15) have been synthesized via hydrothermal route.The structural study reveals that CdO nanostructures possess crystalline phase and cubic structure.The CdO-SnO2 nanocomposites possess both cubic and orthorho
Pure tetragonal 10-20-nm-size zirconia-based Ni-P composite coating was developed.The physicochemical and electrochemical characteristics including corrosion resistance of the coating were investigated.The Ni-P-nano-tetragonal zirconia coating was partial
The gradient mechanical properties,variation of stress with strain and surface cracking behavior of expanded austenite developed on 316L austenitic stainless steel were investigated by nanoindentation tests,X-ray residual stress analysis and scanning elec